Continental Cement is located in the new industrial development area (NIDA) Kanjikode Palakkad. Its installed capacity at 60,000 MT. Our focus was on reducing carbon emissions. Our company has its own quality laboratory for rigorous quality control as per BIS.

We manufacture Portland Pozzolana cement is a kind of cement either by inter grinding OPC clinker and Pozzolana. It is commonly referred to as PPC cement. As the pozzolana materials are very fine, they can fill the gaps between the reinforcement and the aggregate, thus reducing the carbon monoxide emission from the concrete, making it environmental friendly.

Better Strength

Better Durability

Better Workability

Better Bonding

Continental Cement is Portland pozzolana cement (PPC) superior blended cement manufactured by grinding of high quality OPC with fine fly ash from selected electrostatic precipitator (ESP). It is extracted and transported through container to our factory to produce continental cement, with the selected raw material and the desired proportion. We inter ground in a high efficiency manner to enable us to obtain high fineness and good particle size distribution (PSD). Stringent quality measure and advanced inter grinding technology gives a fluid nature and superior bonding.

Vision

To create value on a sustained basis for all stakeholders of continental cements through lofty standards of transparency, and responsibility. Leadership and Innovation in cement manufacturer.

Mission

Continental Cements will strive to remain a leader in the manufacture of cement and establish itself as a preferred supplier of products and services to its clients and enhance the value for all stakeholders. To create value for all delighted customers, enlightened partners, loyal shareholders, and a healthy environment.

  • TEST REPORT OF CONTINENTAL CEMENT (PPC)
  • IS 1489:2015 (PART-1) FLYASH BASED

  • CHEMICAL COMPOSITIONS

    S.NO. PARTICULARS RESULTS OBTAINED AS PER IS 1489:2015 (PART-1)
    1 Loss on ignition, percent by mass –(LOI) 2.5% Not more than 5 %
    2 Insoluble residue- percent  by mass (IR) 29.8 % Addition Of Fly ash Percentage : 34 %
    3 Total sulphur content calculated as sulphuric anhydride –(SO3) 1.8 % Not more than 3.5 %
    4 Magnesia, percent  by mass –( MgO 2.4 % Not more than 6 %
    5 Chloride content, percent by mass. (Cl) 0.01 Not more than 0.05

    PHYSICAL PROPERTIES

    S.NO. PARTICULARS RESULTS OBTAINED AS PER IS 1489:2015 (PART-1)
    1 FINENESS 364 m2/kg Not less than 300M2/kg
    2 SOUNDNESS

    a. Le Chatilier
    b. Auto Clave

    		 1 mm
    0.032%    		 Not more than10mm
    Not more than 0.8 %
    3 SETTING TIME

    a. Initial Setting Time
    b. Final   Setting Time

    		 105 mts.
    195 mts.    		 Not less than 30 Mts.
    Not more than 600 Mts
    4 COMPRESSIVE STRENGT

    a. 3 Days
    b. 7 Days
    c. 28 Days

    		 20 Mpa
    31 Mpa
    42 Mpa    		 Not less than 16 Mpa
    Not less than 22 Mpa
    Not less than 33 Mpa
    5 Drying Shrinkage 0.01 % Not more than 0.15%